The space lattice of a diamond belongs to the cubic system, and its diamond structure has a lattice constant of a=0.3560 nm and a cleavage plane of 111.
Diamond is classified optically as Type I and Type II. Type I shows the absorption bands at 8 and 20.8 mm by the impurities other than the 5 mm absorption band. On the other hand, Type II shows the 5 mm absorption band only. The transmittance of Type II is T=60% for wavelengths longer than 6 mm. There is no other material that shows such an optical property.

??

An allotrope of CARBON. It is the hardest naturally occurring substance and is used for jewelry and, industrially, for cutting and drilling equipment. Each carbon atom is surrounded by four equally spaced carbon atoms arranged tetrahedrally. The carbon atoms form a three-dimensional network with each carbon–carbon bond equal to 0.154 nm and at an angle of 109.5° with its neighbors. In diamonds millions of atoms are covalently bonded to form a giant molecular structure, the great strength of which results from the strong covalent bonds. Diamonds can be formed synthetically from graphite in the presence of a catalyst and under extreme temperature and pressure; although small, such diamonds are of adequate size for many industrial uses.

?? ??

Diamond is the cubic crystalline form of carbon.When pure, diamond is water clear, butimpurities add shades of opaqueness including black. It is the hardest natural material with ahardness on the Knoop scale ranging from 5500to 7000. It will scratch and be scratched by thehardest anthropogenic material Borozon. It hasa specific gravity of 3.5. Diamond has a meltingpoint of around 3871°C, at which point it willgraphitize and then vaporize. Diamonds aregenerally electrical insulators and nonmagnetic.Synthetic diamonds are produced from graphiteat extremely high pressures (5444 to 12,359.9MPa) and temperatures from 1204 to 2427°C.They are up to 0.01 carat in size and are comparableto the quality of industrial diamonds.In powder form they are used in cutting wheels.Of all diamonds mined, about 80% by weightare used in industry. Roughly 45% of the totalindustrial use is in grinding wheels. Tests haveshown that under many conditions syntheticdiamonds are better than mined diamonds inthis application.

DIAMOND ?? ?? ? ???

???

?? ??

DIAMOND ?? ??

???	??	???	??	?? ?	??
Alfa Aesar	400-6106006	saleschina@alfa-asia.com	China	30123	84

DIAMOND ?? ??: