Abstract

Anti-rodent polymer composites were prepared using non-toxic substances denatonium benzoate (DB) and capsicum oleroresin (CO) mixed with polyvinyl chloride (PVC) matrix. DB is mixed in zinc stearate (ZnSt) called DB/ZnSt, and CO, providing burning sensation, is impregnated in mesoporous silica named SiCO. There are three sets of sample: Blank, composites Set I and Set II. Set I consists of DB/ZnSt at concentration of 1.96 wt% and SiCO at concentration of 12.16 wt%, 14.47 wt%, 18.75 wt% and 23.53 wt%. Set II comprises SiCO at the same amount of Set I. The anti-rodent composites studied are anti-gnawing, surface morphology, thermo-mechanical and rheological properties. Anti-rodent testing is analyzed by one-way blocked analysis of variance (ANOVA) and compared with Tukey test with a 95% level of significance, presenting good anti-gnawing efficiency. The best rat-proof sample is II.4, consisting of SiCO 23.53 wt%, which presents percentage of weight loss from gnawing at 1.68% compared to weight loss of neat PVC at 59.74%. The addition of SiCO at concentration ranging from 12.16 to 23.53 wt% reduces tensile strength around 25–50%, elongation at break strength around 2–23%, shear storage modulus (G′) around 30%, shear loss modulus (G″) shear viscosity (η) and glass transition (Tg) around 43% compared to Blank. The increase in SiCO concentration slightly improves the thermal stability of PVC composites around 3%, but the addition of DB/ZnSt at 1.96 wt% slightly reduces those properties.