ChemicalBook CAS DataBase List 3-Chloropropyltriethoxysilane

3-Chloropropyltriethoxysilane synthesis

10synthesis methods

Product Name:3-Chloropropyltriethoxysilane
CAS Number:5089-70-3
Molecular formula:C9H21ClO3Si
Molecular Weight:240.8

(1) Reaction process: Ru-B/γ-Al2O3 catalyst with 0.5% loading was uniformly filled in a fixed bed and purged by nitrogen for 5 min, after which the temperature was raised to 115°C. The reaction was carried out at a speed of 120 r/min with a stirr

998-30-1
254 suppliers
$30.00/25g

107-05-1 Synthesis

107-05-1
422 suppliers
$16.80/100ML

5089-70-3
325 suppliers
$10.00/5g

Yield:5089-70-3 99.44%

Reaction Conditions:

with Ru-B/γ-Al2O3 at 115; for 1 h;Inert atmosphere;Temperature;

Steps:

1.1-1.2; 2.1-2.2; 3.1-3.2; 4.1-4.2; 5.1-5.2; 6.1-6.2; 7.1-7.2; 8.1-8.2; 9.1-9.2 Example 9

(1) Reaction process: a Ru-B / γ-Al2O3 catalyst with a loading of 1.5% was uniformly packed in a fixed bed, purged with nitrogen for 5 minutes, and then heated to 115 ° C. Then 3-chloropropene and triethoxysilane were put into the stirring kettle at a molar ratio of 1: 1.5, the rotation speed of the stirrer was 120 r / min, and the stirring time was 1 h. After mixing, the raw material liquid was obtained. The mixed raw material liquid was passed through a fixed bed at a space velocity of 1.5 g / h / g Cat to obtain a mixed product after the reaction.(2) Purification process: The mixed product after the reaction is passed into a distillation kettle, the temperature of the distillation is first raised to 45 ° C, and then the temperature is increased by 10 ° C every 0.5h, until the temperature is raised to 75 ° C and the distillation is completed in 0.5h. The whole distillation process The pressure was -0.1MP. The bottom material after the distillation was passed into a rectification tower, and the temperature of the rectification tower tower kettle was raised to 150 ° C. and the pressure was -0.1MP. The material at the top of the tower was collected to obtain a product.

References:

CN110551150,2019,A Location in patent:Paragraph 0020-0046; 0053